1.3mm PVC Laminated Tarpaulin – LPT1113/1625

1.3mm PVC Laminated Tarpaulin – LPT1113/1625

Introducing our 1625gsm brown vinyl-coated tarpaulin, engineered specifically for manufacturing industrial-grade PVC flexible water tanks. Its robust foundation is a 1300Dx1500D polyester base fabric with a 30×26 weave density, ensuring exceptional tensile strength and durability for demanding applications.

This material delivers superior barrier and sealing properties, outstanding resistance to chemical corrosion, and excellent adaptability to harsh environmental conditions. It provides a reliable and high-performance solution for your PVC flexible water tank production, guaranteeing the safe and secure transportation of a wide range of liquid cargoes.

LonaTarp® 1.3mm PVC Flexible Water Tank Product Specifications

Fabric Properties	Parameters	Testing Method
■ Technical properties
Total Weight	1625 Gsm/m² 45 OZ/YD²	DIN53352/ BS3424
Base Fabric	100%PES 1300x1500D 30*26/inch	DIN EN ISO2060/ DIN53853
Tensile Strength (warp/weft)	5189/4572 N/5cm	ISO1421
Tear Strength (warp/weft)	1097/1054 N/5cm	DIN 53363
Adhesion	＞170 N/5cm	DIN 53357
Temperature Resistance	-30℃ / +70℃	DIN53372
Number of Flexes	>50,000	DIN53359A
Flammability(Optional)	DIN4102:B1, NFPA701, M2
Max Width	3.2M (10.50Feet)
Application	Flexible Tank
All technical data set out above are for product information purposes only and not legally binding, and will cease to apply with any further development of the products. The most recent technical data will be provided by LonaTarp® on request. Please note that the technical data as set out above are average values only. All values are generated through tests by established laboratories in accordance with industry standards. Results may vary if testing is executed by different laboratories or due to different standard interpretation. All technical data apply to new products only. Deviations may occur due to production procedures.