850Gsm PVC Semi-Coated Tarpaulin – LPT1070/850

850Gsm PVC Semi-Coated Tarpaulin – LPT1070/850

This heavy-duty 850gsm PVC bag fabric is constructed with an 850D 18×20 polyester base, delivering exceptional tear resistance for superior luggage durability. The robust vinyl material ensures your products offer outstanding protection and maintain their structural integrity over time.

Its high weight and density provide excellent abrasion resistance and a pristine, professional finish, making it the ideal choice for manufacturing protective cases and long-lasting travel gear. This reliable material is engineered to meet the demanding standards of bag manufacturers for quality and performance.

LonaTarp® 0.68mm PVC Bag Fabric Product Specifications

Fabric Properties	Parameters	Testing Method
■ Technical properties
Total Weight	850 Gsm/m² 25 OZ/YD²	DIN53352/ BS3424
Base Fabric	100%PES 850D 18*20/inch	DIN EN ISO2060/ DIN53853
Tensile Strength (warp/weft)	1546/1404 N/5cm	ISO1421
Tear Strength (warp/weft)	316/264 N/5cm	DIN 53363
Adhesion	77.65 N/5cm	DIN 53357
Temperature Resistance	-30℃ / +70℃	DIN53372
Number of Flexes	>50,000	DIN53359A
Flammability(Optional)	DIN4102:B1, NFPA701, M2
Max Width	3.2M (10.50Feet)
Application	PVC Bags
All technical data set out above are for product information purposes only and not legally binding, and will cease to apply with any further development of the products. The most recent technical data will be provided by LonaTarp® on request. Please note that the technical data as set out above are average values only. All values are generated through tests by established laboratories in accordance with industry standards. Results may vary if testing is executed by different laboratories or due to different standard interpretation. All technical data apply to new products only. Deviations may occur due to production procedures.